English translation for "退火热处理"
|
- annealing heat treatment
Related Translations:
熔热处理炉: heating treatment funacesheatingtreatmentfunaceshoning machines 退火炭: annealing carbonannealing color 火焰退火: flame annealingflame temperingtorch annealing 碳化物退火: carbide annealingcarbide-base cermet 双重退火: double annealingduplex annealing
- Example Sentences:
| 1. | The formation of a new set of strain - free grains within a previously cold - worked material ; normally an annealing heat treatment is necessary
在冷塑性变形材料的内部生成等轴状新晶粒的过程叫再结晶，通常发生于再结晶退火热处理过程中。 | | 2. | It has been found that a preferable orientation can be obtained while both the smco5 phase and the sm2co17 phase have deposited plenty in the two - steps heat treatment
而合适的两级退火热处理能使smco5和sm2co17永磁相充分析出,并形成一定的择优取向,从而可以显著提高薄膜的矫顽力。 | | 3. | The results showed that the microstructure of as - deposited tbdyfe ii 1ms were amorphous and the crystal of tbfe2 were found in films after annealing at 500 . annealing films in vaccum could improve the saturation magnetization ms and the susceptibility , decrease the coercivity and the saturaion field , and make the direction of the magnetic moments parallel to the film plane
结果表明，制备态薄膜为非晶态结构，经过500真空退火热处理后，薄膜出现了tbfe _ 2的结晶物，薄膜的矫顽力和外场的饱和磁场大大降低，饱和磁化强度增强，初始磁化率提高，易磁化轴转向膜面。 | | 4. | The better magnetostriction of tbdyfe thin films was 120x 10 - 6 in 100ka / m and 240 x 10 - 6 in 330ka / m the research on the magnetostriction of smco / tbdyfe bilayer films indicated that smco thin films could improve the magnetostricion of tbdyfe thin films effectively through improving its saturation magnetization ms and susceptibility
退火热处理和衬底粗糙度的降低有助于薄膜磁致伸缩性能的提高。对smco tbdyfe复合薄膜磁致伸缩特性的研究表明， smco薄膜的复合能提高磁致伸缩薄膜的磁化率和饱和磁化强度从而提高tbdyfe薄膜磁致伸缩性能。 | | 5. | X - ray diffraction results revealed that the structure of as - deposited smco film was amorphous and crystallization happened after the films annealed at 500 in vacuum . the magnetic tests of smco thin films showed that its coercivity reduced with the increase of film ' s thickness while the ratio of mr / ms was opposite . the films " coercivity and mr / ms declined after it annealed at 500 because the machanism of magnetization were changed from domain wall nailing into magnetic nuclear forming
研究结果表明，由于杂质fe的掺入降低了smco薄膜的磁性能；制备态smco薄膜为非晶态结构，矫顽力hc随着薄膜厚度的增加而减小，剩磁比mr ms随膜厚增加而增加；经过500真空退火热处理后，薄膜出现smcos的结晶物，矫顽力hc降低， mr ms减小，磁化机制由畴壁钉扎类模型转为形核类模型。 | | 6. | Analyses showed that the effect of heat treatment is remarkable to 304 stainless steel fibers . and a new martensitic phases formed , and ms increased during annealing at 180c ; annealing above 180c decreased the ms . after annealed in the range of 380c ~ 440 c , the he increased and the product ( mr hc ) improved . it was also shown that annealing affected the mechanical properties of 316l ss fibers obviously
304不锈钢纤维在180附近退火处理其ms略增加，其内部相变与一般的304不锈钢体材料存在差别； 380 440区间退火处理，其矫顽力急剧增加、磁能积参数配合比较好；退火热处理对316l不锈钢纤维的力学性能作用明显。 |