| 1. | Using burnability index to control the burning temperature of rotary kiln
用生料易烧性指数控制回转窑煅烧温度 |
| 2. | Polycrystalline structure of waste slag in aluminum factory at different calcining temperature
铝厂污泥在不同煅烧温度的晶相结构研究 |
| 3. | Influences of temperature on the structure of kaolinite and its electric insulation properties
煅烧温度对高岭石结构及电绝缘性能的影响 |
| 4. | A summary of mgo ' s burning temperature and the relationship with miniature swelling performance
氧化镁煅烧温度与其微膨胀性能关系的综评 |
| 5. | If the sintering temperature was lower than the reaction temperature , phase separation will develop
煅烧温度低于反应物的固相反应温度时，只能导致前驱物分相。 |
| 6. | The effects of calcinations temperature and holding time on the perovskite phase of synthesized pmn - pt have been studied
并研究了煅烧温度及保温时间对合成材料单相性的影响。 |
| 7. | Based on the dta / tg and tem patterns , we chosed 450 c as the lowest temperature and 2 hours as the shortest time for calcining
根据dta tg和tem分析结果，我们选定凝胶的最低煅烧温度为450 ，最低煅烧时间为2小时。 |
| 8. | Considering energy conservation and effects of calcined kaolin on the strength of cement , it was optimum method to produce calcined kaolin by calcining it at 980 c for 0 . 5h and then cooling it suddenly
结合煅烧高岭土对水泥强度的影响，考虑到节约能源，以采用980恒温0 . 5h然后快速冷却的方法作为最佳煅烧温度与时间。 |
| 9. | Compared with 3 % , the temperature of polymorphic transition between anatase and rutile of 8 % which is the molar quantities of mixed rare earth is a little lower . the calcination temperature is a main reason which influences the structure of phase
掺入镝的含量8时，锐钛矿相向金红石相的转变温度与3相比有所降低，所以煅烧温度是影响产物结构的主要原因。 |
| 10. | Abstract : in this paper , the preparation of the catalysts for the oxidation of fluorene to fluoreone is studied . the influences of the dipping time , calcining temperature , calcining time and the air quantity during the calcination are discussed
文摘:研究了用工业芴气相氧化制取芴酮的催化剂制作条件，考察了浸渍时间、煅烧温度、煅烧时间和煅烧空气量对催化剂制作的影响 |