| 1. | Tenacity increases with increasing heating temperature
样品的韧性随烧结温度的提高而增加。 |
| 2. | The sintering shrinkage increased with increasing sintering temperature
烧结温度的升高提高了烧结收缩率。 |
| 3. | Available with a range of firing temperatures , to suit specific part process conditions
烧结温度范围广,适合玻璃不同方式的加工条件 |
| 4. | The sintered temperature was one of key parameters to the relative density and grain size
烧结温度是决定烧结体致密度高低的主要因素。 |
| 5. | Study of the relation between electromagnetic parameter and sintering temperature of low loss mn - zn ferrite
铁氧体电磁参数与烧结温度的关系研究 |
| 6. | Sintering temperature , type and amount of rare earth were found . 2
比较上述因素的影响程度，优选出最佳烧结温度、最合适的稀土种类及添加量。 |
| 7. | Relation between properties and sintering temperature in the fabrication of new si3n4 ticnano composite ceramic materials
复合陶瓷材料的性能与烧结温度的关系 |
| 8. | Finally , an expert controller ' s design of sintering temperature of industrial rotary kiln is discussed
论文的最后给出了一个工业回转窑烧结温度专家控制器的设计。 |
| 9. | The results show that the grain size of cosb3 grows with increasing sintering temperature or sintering time
结果表明：随着烧结温度的增加和烧结时间的延长，烧结体的晶粒有明显长大。 |
| 10. | Si1verloaded diatomite is manufactured by mixing diatomite with silver nitrate and then sintering at above 450
摘要将矽藻土与硝酸银混合，当烧结温度超过450后，可制得载银矽藻土。 |