Chinese translation for "淬硬层"

quench-hardened case

Related Translations:

淬:  动词(淬火) temper by dipping in water, oil, etc.; quench

软淬:  mild quench

端淬:  end quenching

淬硬性:  hardenability

淬硬:  [冶金学] harden; quench(ing)

冯淬:  feng cui

淬裂:  chill crackhardening crackquench crackingquenchcracking

上淬:  up-quenching

水淬硬:  water quenching

寒冷冷淬:  chill

Example Sentences:

	1.	Effects of laser hardening technical parameters on hardened depth of t10 steel 10钢淬硬层深的影响
	2.	Meanwhile , the fracture was accelerated due to the uneven surface hardness and the unreasonable distribution of the hardening layer on the crankshaft , and the bad lubrication condition in service 同时轴左颈表面硬度不均匀、淬硬层分布不甚合理，工作过程中润滑条件差，加速了曲轴的断裂。
	3.	Moreover , it showed that the linearity rising relations were existed between the laser power and the thickness of hardening layer , and the linearity negative rising relations between the scanning velocity and peak rigidity 此外，结果还表明激光功率与淬硬层厚度成线性增长，而扫描速度与峰值硬度成线性负增长关系。
	4.	The result shows that the quenching inductor with wimble magnet inlaid is adaptable for this technique , and the vertical quenching machine can be used in mass production 结果表明，带锥角镶嵌导磁体的圈式感应器，其有效圈高度、锥角和内径的合理匹配可以满足淬硬层形态的要求，采用立式淬火机床连续淬火可以大批量生产合格的半轴。
	5.	Moreover , a method for iterating thermal and magnetic analysis is put forward . in chapter 5 , the distributed characteristics of eddy and temperature fields in induction heating process are simulation by fem respectively , including the distributions of eddy and temperature fields during the whole induction heating process , the influence of frequency and magnetic disperse , and the prediction of hardened depth 第五章:用ansys软件对感应加热过程中工件内涡流场、温度场的一些基本问题进行模拟及分析，主要包括:加热过程中工件涡流功率密度及温度分布规律;频率与磁力线逸散对加热效果的影响;同时对感应淬火淬硬层深度进行了模拟预测。
	6.	Considering different microstructures and properties of metal of hardened layer and the core of back - up roller , the distributions of shear stress below surface and the contact stress between work roller and back - up roller of a four - high - mill were simulated with nonlinear fem 摘要考虑轧辊表面淬硬层与其心部金属材料组织性能的差别，采用非线性有限元方法对四辊轧机的工作辊与支撑辊间接触应力及辊内剪应力分布进行模拟，并将模拟结果与传统强度校核方法进行了对比分析，研究了轧辊淬硬层厚度对辊间接触应力的影响规律。