| 2. | The propagation characteristics of msfvws in a double - layered yig waveguide
波导中静磁体波的传播特性 |
| 3. | Measurement of magnetic properties of yig single crystal magnetic - films
钇铁石榴石单晶磁性薄膜磁特性的测量方法 |
| 4. | In this paper , yig and ce : yig were prepared via chemical synthesis method , and their composition , structure , magnetic properties were investigated
本文在充分分析本领域国内外研究现状的基础上，采用化学合成法制得单相yig和ce ： yig ，并对其组分、结构特征和磁性能进行了分析研究。 |
| 5. | The investigation of synthesis , composition and structure analysis , and characterization of magnetic properties of yig and ce : yig would build foundation for the study of ce : yig single crystal in the future
Yig和ce ： yig的合成及其成分、结构和性能的分析，为ce ： yig单晶的制备和研究奠定了良好的基础。 |
| 6. | Vibrating samples magnetometer ( vsm ) testing implied that yig were of ferrimagnetism , and cerium substitution had effects on saturation magnetization ( ms ) , residual magnetization ( mr ) and coercive force ( hc )
Vsm测试结果表明yig属于亚铁磁性物质， ce离子的掺杂对饱和磁化强度( ms ) 、剩余磁化强度( mr ) 、矫顽力( hc )都有一定的影响。 |
| 7. | The results of x - ray photoelectron spectrum ( xps ) demonstrated the ce ions in pure phase ce : yig ( x < 0 . 2 ) were in the state of trivalence . scanning electron microscope ( sem ) analysis showed conglobation of yig and ce : yig particles , whose size were smaller than 1 urn
Xps的分析结果显示单相ce ： yig ( x 0 . 2时)中ce离子是以正三价的状态存在，这与物相分析结果是一致的。 |
| 8. | Yig and ce : yig precursors were prepared via coprecipitation . by means of improving homogeneity and decreasing synthesis temperature , harmful yfeo3 phase was restrained , the oxidation of ce3 + was under control , and pure phase yig and ce : yig ( x = 0 . 2 ) were obtained
采用共沉淀法合成yig及ce ： yig前驱体，通过提高组分均匀性、降低煅烧温度等手段，有效地抑制了yfeo _ 3杂相的生成和ce ~ ( 3 + )离子的氧化，合成了单相yig和ce ： yig 。 |
| 9. | Cerium - substituted yttrium iron garnets ( cexy3 - xfe5o12 , ce : yig ) , the promising materials for magneto - optical ( mo ) application , have been widely attended for great improvement on faraday rotation due to the substitution of ce3 + ions to y3 + ions . however , studies on synthesis of ce : yig were restrained by two factors : the first was radium of ce3 + ions were much larger than that of y3 + ions , the second was ce3 + ions tended to transfer to ce4 + ions which were more chemically stable
掺铈钇铁石榴石( ce - substitutedyttriumirongarnets ，简称ce ： yig )中，由于ce ~ ( 3 + )离子对y ~ ( 3 + )离子的取代，将大大提高钇铁石榴石( yttriumirongarnets ，简称yig )磁光材料的法拉第旋转角和磁光优值，使其能够广泛应用于激光和光通信等高技术领域。 |
| 10. | The bragg diffraction efficiency of gows in bismuth - doped yig film is caculated by considering the edge cut - off effect . the obtained theoretical curve is basically agreement with the experimental results . it is shown that the diffraction performance for mo bragg cells can be greatly increased by using an appropriately nonuniform bias field
2 .考虑到边缘截止效应,论文中计算了静磁正向体波对导波光的衍射效率,理论结果与实验符合;从而表明,与均匀场情形相比,适当不均匀场可以大大提高磁光bragg器件的衍射效率。 |