再结晶退火 meaning in English
recrystallization annealing
recrystallizational annealing
Examples
- A satificatory effect is obtained by rime annealing
采用再结晶退火工艺处理，可取得满意效果。 - The formation of a new set of strain - free grains within a previously cold - worked material ; normally an annealing heat treatment is necessary
在冷塑性变形材料的内部生成等轴状新晶粒的过程叫再结晶，通常发生于再结晶退火热处理过程中。 - Low cycle fatigue ( lcf ) behavior of zircaloy - 4 has been reviewed in the present paper . then , the lcf behavior of a recrystallized zircaloy - 4 plate with different texture has been studied at room temperature and 400 , respectively
并在此基础上，研究了不同温度(室温和400 ) 、不同取向(平行于轧向和垂直于轧向)的再结晶退火态zr - 4合金板材试样的低周疲劳性能。 - Zircaloy - 4 sheet , which was cold - worked followed by recrystallization annealing , exhibits longer lcf life in the rolling direction than that in the transverse direction , and the fact that difference in lcf life between both directions becomes larger as the range of plastic strain becomes lower can be attributed to the texture effect , p - solution treatment deteriorates the alloy ' s lcf property because the treatment lowers the average value of alloy ' s schmid factors , and the subsequent annealing - treatment in a - phase range has a impact on the lcf properties , i . e . the subsequent annealing - treatment at 500 ? for 1 . 5h results in better property than that at 750 for 1 . 5h , which comes mainly from the fact that the alloy annealled at 500 for 1 . 5h has lower amount of the precipitate particles than the alloy annealled at 750 for 1 . 5h
对于冷加工后经再结晶退火处理的zr - 4合金，轧制方向的低周疲劳寿命比横向要大。随着_ p的降低，两个方向的低周疲劳寿命的差别相应增加，这是由于合金中存在织构的缘故。冷加工后经再结晶退火处理的zr - 4合金在固溶处理后，抗疲劳性能明显降低，这主要是由于固溶处理降低了合金的schmid因子；固溶处理后在相区的退火对疲劳性能有影响，即500 1 . 5h退火的抗疲劳性能要优于750 1 . 5h退火，这主要与500 1 . 5h退火的合金中沉淀相粒子的数量较少有关。 - The alloys , which were cold - worked followed by recrystallization annealing , display cyclic softening in the range of low strain because the cyclic stress - strain curve lies below the monotonic stress - strain curve , and show cyclic hardening in the range of high strain because the cyclic stress - strain curve lies above the monotonic stress - strain curve
在低应变范围，冷加工后经再结晶退火处理的错合金的循环应力一应变曲线位于单调拉伸曲线的下方，表现为循环软化;在高应变范围则位于单调拉伸曲线的上方，表现为循环硬化。