| 1. | Magnetic field strength h of sintered smco magnet
烧结钐钴磁铁的最低饱和磁化磁场强度 |
| 2. | Powder metallurgy . hard metals . determination of specific saturation magnetization
粉末冶金.硬金属.饱和磁化强度的测定 |
| 3. | Standard test method for saturation magnetization or induction of nonmetallic magnetic materials
非金属磁性材料的饱和磁化或磁导的标准试验方法 |
| 4. | The coercivity and the magnetization of the sample reduced at 900 were 2270e and 48 . 2 emu / g
经900还原的样品矫顽力较小，比饱和磁化强度较大。 |
| 5. | ( 9 ) the coercivity of the sample submitted to reduction at 700 was 488 oe , and the magnetization was 17 . 8emu / g
( 9 )经700还原的样品矫顽力较大，比饱和磁化强度较小。 |
| 6. | The saturation magnetization of the sample is 1 . 79t close to the theoretical value of the same composition alloy
试样的饱和磁化强度为1 . 79t ，接近相同成分下合金的理论磁化强度的数值。 |
| 7. | For an amount of substitution 0 < x < 0 . 6 , the znti substituted ferrite showed higher values of both coercive field strength and saturation magnetization than znir substituted phase
在0 x 0 . 6范围内， znti代换的样品比饱和磁化强度和矫顽力比znlr代换的要高。 |
| 8. | Scientists have been devoting to enhance the density of magnetic recording media for years . magnetic materials are expected to be with high coercivity and high saturation magnetization
提高磁记录介质的密度是人们多年所追求的目标，这要求磁性材料具有高矫顽力和相应的高饱和磁化强度。 |
| 9. | By controlling parameters superparamagnetic magnetic composite microspheres with size less than 300nm , magnetic content 24 % and saturation magnetization 47emu / g could be prepared by miniemulsion polymerization
用该法制备的磁性复合微球磁含量可达22 %以上，饱和磁化强度可达犯. sem川g 。 |
| 10. | Clients who require non - magnetized smco permanent magnet must be acquaint with self - magnet equipments for the purpose of completely satiate and magnetize our products or codes
需要提供不充磁钐钴永磁体的用户，一定要熟悉自己的充磁设备的充磁能量，以便选择可完全饱和磁化本公司产品的牌号。 |