By framing reasonable technology and plenty of repeating experiment , the main contributions have been made as follows : 1 ) the analysis of differential scanning calorimetry ( dsc ) was made on the bmi resin , qy8911 - ii . curing reaction of the qy8911 - ii was studied by dsc . the effect of heat history on the resin was discussed and the adequate parameters for filament winding technology were determined . 2 ) the study on preparation technology of prepreg strands was carried out
通过制定合理的工艺和大量的反复实验，主要完成了以下三方面的工作： 1 )针对缠绕工艺特点，对qy8911 -双马来树脂进行了差示扫描量热法( dsc )分析，通过测试数据及对大量数据分析，确定了用qy8911 ?进行加热缠绕的合理工艺窗口，指明了用qy8911 -进行加热缠绕工艺的可行性； 2 )开展了预浸纱制备工艺实验研究，通过反复调试获得了满意的工艺参数，制备出了满足工艺要求的预浸纱，为m46j / qy8911 -缠绕复合材料的研制奠定了基础。