韧转变 meaning in Chinese
brittle ductile transition
Examples
- Eoc and caco3 were combined to toughen and reinforce pp to study the effect of factors such as the composition , the diameter and shape of filler , the nature of elastomer , dispersing morphology and matrix type on the properties of pp / eoc / caco3 composites
结合起来增韧增强聚丙烯,研究了组成比、填料粒径及形状、弹性体性质、分散形态和基体类型等一系列因素对pp用occaco3复合材料性能的影响,揭示该体系发生脆韧转变的基本条件是l人( 。 - The impact behaviors of pp / eoc and pp / caco3 were compared . the toughening mechanisms of pp / eoc and pp / caco3 systems are firstly proved to agree well with wu ' s percolation theory . the essential condition occurring brittle - tough transition in two binary systems is that the matrix ligament thickness ( l ) is lower than the critical matrix ligament thickness ( lc ) which is approximate to 0 . 095 ? m
比较ppffioc和ppcacos二体系的增韧行为,发现加入eoc和cacos都能增韧pp ,首次验证了新型弹性体eoc和无机刚性粒子cacos增韧pp的机理符合wu氏逾渗理论,二体系发生脆韧转变的基本条件是基体带厚度l小于临界基体带厚度人( 。 - The results revealed that the essential condition occurring brittle - tough transition in such ternary system was l ? lc ( ? 0 . 095 ? m ) , and the effect of above factors on the impact behavior followed percolation mechanism which indicated that it was some reasonable using lc as single parameter criterion of brittle - tough transition of pp / eoc / caco3 composites . the micro - deformation model at different dispersing morphology was then proposed
首次将聚合物复合材料脆韧转变机理的定量化研究从二元体系拓宽到三元体系,对ppffioc aco3体系的配方进行设计,制备得到高刚性高韧性低成本的聚丙烯复合材料, eoc和cvco3的体积份数之和为25v (其中弹性体相为10v 。