还原温度 meaning in Chinese
reduction temperature
Examples
- The better deoxidation parameters are also obtained according to these relative experiments , 510 is the better temperature and 2 . 5 hours are the better deoxidation time
通过实验结果和理论分析，得到了fec _ 2o _ 4 . 2h _ 2o还原制备超微纯fe粉较佳还原工艺参数为还原温度510左右，还原时间2 . 5h左右。 - Under the condition of 1000 ~ 1200 , study the effect of the carbon - bearing pellet strengths and metallization rate with different iron ore concentrate size , matching carbon ratio ( carbon oxygen mol ratio ) , kind of additive and reduction temperature
摘要在1000 ~ 1200条件下研究了不同的矿粉粒度、配碳比、粘结剂、还原温度等对含碳球团强度及金属化率的影响。 - Abstract : the technologic factors which influence the composition of iron powder are investigated , such as secondary reduction temperature , time , scale thickness . the available technologic systems that are employed to produce high quality iron powder are brought forward
文摘:研究了二次精还原温度、时间、生粉料层厚度等工艺因素对铁粉化学成分的影响，提出了工业生产高品位铁粉的合理工艺制度。 - By analyzing the thermal decomposition mechanism of fec _ 2o _ 4 . 2h _ 2o precursor , we mainly carried out the experiments of the influence of the deoxidation temperature to the appearance of sfp of fe , the influence of the deoxidation time to the appearance of it
Fec _ 2o _ 4 . 2h _ 2o还原制备超微纯fe粉实验部分，进行了还原时间对前驱体还原程度影响实验，以及还原温度对超微fe粉颗粒形貌影响实验。 - By considering the effect of different binders , basicity , reduction temperature and time on the compression strength and dezinc degree after reducing , find out the best scheme a1b3c3d3 and get the metallic pellets with higher compression strength and dezinc degree
通过研究不同粘结剂、碱度、还原温度和还原时间对熟球抗压强度、脱锌率的影响，找出最佳试验方案为a1b3c3d3 ，得到脱锌率和抗压强度较高的金属化球团。