解理断裂 meaning in Chinese
cleavage fracture
Examples
- Cleavage fracture strength
解理断裂强度 - Quasi - cleavage fracture
准解理断裂 - Influence of loading rate on critical event of cleavage fracture in notched specimen of low alloy steel
加载速度对低合金钢缺口试样解理断裂临界事件的影响 - With carbon content increasing , the carbide network on the fertile grain boundary sprouting and propagating . the fracture mode has been changed from cleavage to along boundary and the intergranular corrosion induced by solution chromium decreasing
随碳含量提高，晶界上碳化物萌发、扩展呈网状，铸件脆断由解理断裂发展为沿晶断裂，同时铁素体不锈钢晶间腐蚀倾向增大。 - The fractorgraphy analysis show that in the layer rich in w and mo , the feature of fracture is brittle fracture which follow the bordline of crystal . in sections rich in the felt metal , the feature of fracture is ductile fracture . in w - mo layer , the feature of fracture are brittle fracture and some ductile fracture
断口形貌特征研究表明，富w区、富mo区主要为沿粒界脆性断裂；粘结金属发生韧性断裂； w - mo混合区为颗粒的沿粒界脆性断裂和粘结相的韧性断裂的混合型断裂；富ti区为典型的穿晶解理断裂； mo - ti混合区以穿晶解理断裂为主，颗粒边界表现出准解理断裂特征。