- It is known that high intense pulsed ion beams ( hipib ) have a high viability to be used as an efficient energetic source for rapid film deposition and direct surface modification . up to now , however , there is still lack of a systematic work to reveal the influence of hipib on the film deposition and material modification although there are lots of papers have been published in the field . in the present work , these two practical applications of hipib were all investigated in detail
根据强流脉冲离子束( highintensepulseionbeam ? hipib )技术具有快速沉积薄膜和材料表面辐照处理改性的特点,而目前对其薄膜沉积和材料辐照处理缺乏系统研究,本论文的工作分为两部分,其一是类金刚石薄膜( diamondlikecarbon ? dlc )沉积,其二是高速钢直接辐照处理表面改性。 - In the hipib strengthening experiments , samples of high - speed steel ( w6mo5cr4v2 ) were irradiated by abstract hipib ( cn + = 30 % , h + = 70 % , ion energy 250 kev , ion current density 60 - 180a / cm2 , pulse duration 80 - 100 ns ) . microstructure investigation and properties characterization of the treated hss samples were carried out to investigate the effect of current density and pulse number of incident hipib on the surface modification treatment . the physical mechanism of the hipib - solid interaction was established based on the experiments
在hipib轰击材料表面方面,本文选择成分由c ~ ( n + ) ( 30 )和h ~ + ( 70 )组成、加速电压为250kv 、脉冲宽度为80 100ns的hipib对高速钢( w6mo5cr4v2 )进行表面辐照处理,研究离子束流密度和脉冲次数对高速钢微观结构和宏观性能的影响,探讨了hipib与材料表面相互作用的物理机制。