粉煤灰陶粒 meaning in Chinese
lytag
Examples
- Research on high - strength sintered fly ash aggregate and lightweight aggregate concrete
高强粉煤灰陶粒的研制及其混凝土试配 - Using fly ash as the main material along with a proper quantity of clay and admixture , the experiment is conducted to produce lytag through sintering the mixture
本实验以粉煤灰为主要原料，适量添加粘土及外加剂，用烧结法制备粉煤灰陶粒。 - After the sample is turned out , its internal and external structures are observed and its bulk density is measured in order to determine how the sintering temperature , the time of thermal preservation , and the quantity of admixture affect the performance of lytag
通过对试样内、外部结构观察和容重的测定，研究烧成温度、保温时间及外加剂掺量对粉煤灰陶粒性能的影响。 - It is made of sand , cement and lightweight aggregate , etc . some of the lightweight aggregates include pumice , stuff , expanded clays ( haydite ) , etc . lightweight aggregate concrete can provide the same strength as the normal concrete with less weight
轻骨料混凝土是一种用量较大的新型混凝土，其密度在850kg m ~ 3至1950kg m ~ 3之间，由粘土陶粒，粉煤灰陶粒等粗骨料以及常用的砂，水泥，水等材料制作而成。 - The author of this article used orthogonal test design , arranged the test scheme scientifically , selected material carefully , at last yielded an high strength lightweight aggregate concrete material ( hslacm ) , whose compressive strength exceeded 50 mpa and quality under 1950kg / m3 , mainly by using 42 . 5 ordinary portland cement , expanded fly ash aggregate , silica fume , superplasticizers and so on
本文是在广泛阅读国内外有关资料的基础上，采用正交设计，科学地安排试验，精心选材，用42 . 5普通硅酸盐水泥、粉煤灰陶粒、硅灰、高效减水剂等材料，采用一般工艺配制出了一种抗压强度超过50mpa 、质量低于1950kg m ~ 3的高强轻骨料混凝土材料。