- Increasing consistence in a limited range could decrease the v when epdm was chosen to be the compatible
以epdm为增容剂，结果表明相容性在一定范围增加可以减小泊松比值。 - The izod impact strength was increased 48 % and the tensile strength was increased 12 % contrast with pure pp , achieved the highest value when 3 % nano - sio2 by weight modified with silicone coupling agent and pp - g - mah was added
加入3纳米sio _ 2粒子，复合增容剂5份时复合材料力学性能最佳，相比纯pp其冲击强度提高48 、拉伸强度增加12 。 - The nanocomposites with exfoliated structure composed of low density polyethylene ( ldpe ) , of organically modified montmorillonite and ethylene vinyl acetate copolymer ( eva ) were prepared through two steps melt intercalating technique using a twin - screw extruder
采用两步法熔融插层工艺，在双螺杆挤出机上制备了以乙烯?醋酸乙烯共聚物( eva )为增容剂的低密度聚乙烯( ldpe )基蒙脱土纳米复合材料。 - In this thesis two kinds of coupling agents and maleic anhydride ( mah ) grafted polypropylene ( pp - g - mah ) were employed to act as interface compatibilizers for pp / nano - sio2 . master batches from pp ( 90 ) , nano - sio2 ( 10 ) and coupling agent ( 1 ) were prepared by twin - screw extruder firstly
本课题选用硅烷偶联剂、钛酸酯偶联剂以及自制的马来酸酐接枝聚丙烯作为pp sio _ 2复合体系的界面增容剂，采用母粒法挤出工艺制备了改性pp 。 - The composites with different compatibilizers and nano - sio2 content were characterized by means of mechanical testing , differential scanning calorimetry ( dsc ) , x - ray diffraction ( xrd ) , fourier transformation infra - red spectroscopy ( ft - ir ) , transmission electron microscope ( tem ) , scanning electron microscope ( sem ) , etc . the relation between the structure and property of the composites was discussed in this thesis
研究了不同增容剂、纳米sio _ 2含量对复合材料的冲击强度、拉伸强度等力学性能；并利用差热扫描量热分析( dsc ) 、 x射线衍射谱( xrd ) 、红外吸收光谱( ir ) 、扫描电镜( sem )等分析，讨论了复合材料结构与性能的关系。