- The experiment results indicated that conditional on transforming layer 1mm thick and absorbing layer 2mm thick , the combined materials which were processed by 600 and 800 respectively have good absorbing performance , and the influence of the combing sequence on absorbing performance is indistinctive
实验表明，当变换层为1mm ，吸收层为2mm时，以600处理的和800处理的材料进行不同组合都有较好的吸波性能。 - Based on experiment the materials with different content will obtain different absorbing performance . by the experiment , the paper obtained the laws for good absorbing performance . at the same time , the experiment optimized the preparation technology for the better performance
为了应用目的，本文对不同产地原材料、不同含量对材料吸波性能的影响进行了研究，发现兰州产地原材料性能较好；高含量的吸收层和变换层组合才有优异的吸波性能。 - The combination absorbs microwave well with the least reflectivity of - 31 . 59db , and minimally having 2 . 31ghz - frequency band . these results illuminated the directional law of combined materials , it is that , when the double deck with the different thickness , no matter what is absorbing or transforming layers , its absorbing performance would not be influenced on the whole . when the double deck with the same thickness , the combining sequence of materials would cause crucial influence on its absorbing performance
在8 . 2 12 . 4ghz频段内，最小反射率达- 45 . 93db ，有效频宽为4 . 0ghz ；当变换层和吸收层厚度相同，总厚度为2mm时，要获得较好的吸波性能，必须以高温处理的材料作变换层，低温处理的材料作吸收层，即存在材料组合的方向性，其中以1000分别与600 、 700处理的材料组合性能最佳，其最小反射率为- 31 . 59db ，有效频宽最小为2 . 31ghz 。 - About the combination of three layers , for the better absorbing performance , we need select the material treated by high temperatures of 1000 ? ^ 700 ? > 600 ? respectively . the combination with about 2mm thickness had better absorbing performance with the least reflectivity under the - 42db and almost coating the total width of 8 . 2 ~ 12 . 4ghz
对于三层样品组合来说，以1000处理的材料作变换层， 600和700处理的材料作吸收层，总厚度在2mm以下，在8 . 2 12 . 4ghz范围内其最小反射率为- 42db ，有效频宽达到3 . 56ghz 。