- We realized controllable operation and in - situ visualization in the process of the visible light - induce domain switching
发现晶体的反转电压随光强增大而下降,最大降幅达到70 %左右。 - The relation of light intensity and the domain switching voltage of the near - stoichiometric mg - doped lithium niobate was studied
摘要研究了在可见光诱导条件下的近化学计量比掺镁铌酸锂的反转电压与光强之间的关系。 - The method to determin reversal electric field was provided , and on the base of experiment data in this method , a new periodicity poled waveform and period was designed
根据该方法的实验数据设计出了一种新的周期性极化波形和周期。实验的结果有:通过实验测出了slt晶体的极化反转电压为1 . 6kv / mm 。 - Using switching voltage of 5v and measuring voltage of 5v under a bipolar pulse of 1mhz in frequency , the plt ( 14 ) film showed no noticeable changes after being subjected to 3 109 read / write repetitive cycles
在反转电压5v ,脉冲频率为1mhz的测试条件下,经过3 10 ~ 9读写循环后,基本没有疲劳现象发生。 - We studied the mechanism of the visible light - induced domain switching in the lithium niobate crystals , and considered that the main factor is the movement of light - induced carrier , which modified the local electric field in the crystals and then resulted in the reduction of the domain switching voltage
探寻了可见光诱导铌酸锂晶体畴反转的形成机制,认为光诱导晶体畴反转的主要原因是光激载流子迁移改变了晶体内部的局域电场,造成了晶体极化反转电压的降低。