剥离现象 meaning in Chinese
exfoliation phenomenon
Examples
- It was found that only intercalating nanocomposites be prepared by melt polymerization , and the organoclays deintercalated when curing took place
实验表明熔融聚合只能得到插层型纳米复合材料，并且随着固化程度的提高，粘土将会发生脱剥离现象。 - Aramid filaments are treated by a low - temperature plasma with different treatment times . the surface of filaments is observed by sem and the results show that the filament surface is smooth before the treatment and becomes more rough if filaments are treated for 6 minutes . in addition , it is found that the filament peels after 9 minutes of plasma treatment
本课题采用低温等离子体对芳纶纤维进行表面处理后，用sem观察纤维表面，发现未经等离子体处理的纤维表面比较光滑；等离子体处理6分钟后，纤维表面变得粗糙，产生很多微小的刻蚀坑；等离子体处理9分钟后，纤维表面受到的刻蚀程度明显增加，并产生表面剥离现象。 - The modulus and strength of pet / mmt fiber were lower than those of pure pet fiber . this is probably because the lamellar montmorillonite does not disperse randomly and completely , and besides , the spinning and drawing process in our research is limited to make the montmorillonite layers better oriented along the fiber
但pet mmt复合纤维的模量及断裂强度比纯pet纤维稍有下降，这是因为在pet mmt复合材料中蒙脱土片层还没有达到理想的无规分散，存在一定的团聚及未完全剥离现象，此外现有的纺丝拉伸工艺还不能使蒙脱土片层在纤维纵向形成很好的取向。