初始放电 meaning in Chinese
initial discharge
Examples
- The doped material performed well electrochemical property for cycling . the initial discharge capacity of doped material was 165mah / g . after 80 cycles , the capacity loss was about 20 %
使用溶胶凝胶法对层状limno2进行2 % al3 +的掺杂改性,初始放电容量可达165mah / g , 80次循环后衰减约20 % 。 - When the hydrogen storage alloy electrodes are treated by hydrophobic method , preliminary discharge capacity and voltage plateau are improved , however , preliminary discharge capacity and voltage plateau decline with the increase of hydrophobic concentration
贮氢合金电极在用1 ptfe乳液憎水处理后，初始放电容量、电压平台性能有所改善，但随着浓度的进一步增加，这两种性能反而降低。 - Secondly , better performance lifepo4 / c composite was synthesized by adding proper content of sucrose to the reactants , test results exhibited the initial discharge capability could get 130mah . g - 1 and the capability didn ’ t fade down after more than ten cycles ’ test
2 .添加适量的蔗糖制备出电化学性能良好的lifepo _ 4 / c复合的正极材料,其初始放电比容量高达130mah . g - 1 ;经10次充放电循环,材料的比容量几乎不衰减。 - Under the microwave calcination , the optimum time of the microwave sintering was ten minutes . the test of the electro - chemical performance showed the initial discharge capability could reach 118mah . g - 1 , which was 20 % more than that synthesized by conventional sold - phase synthesis
电化学性能测试表明:微波合成的锂离子正极材料lifepo _ 4的初始放电比容量可达到118mah . g - 1 ,比传统高温固相法制备出的材料高出近20 % 。