Due to the formation of low melting calcium - aluminates the corrosion resistance and hot erosion strength are reduced
由于低熔点的铝酸钙的形成，火砖的抗腐蚀能力和抗热蚀强度降低了。
The main results are shown as follows : 1 . bt _ 4 doped with cuo could be sintered in a lower temperature , because cuo has a low melting point . there isn ’ t any other phase in the samples . the dielectric properties decreased because cuo was non - crystalloid
本人工作的主要研究成果如下: 1 . bt _ 4掺杂低熔点的cuo能降低样品的烧结温度,没有其他相生成,烧结后cuo以无定形态的形式存在,导致样品介电性能降低。
The result of the xrd , sem and tem analysis show that the densification process was controlled by the mechanical of liquid phase sintering with the addition of mgo and ce02 as the sintering aid . the mgo - ceo2 would react with the sio2 which was on the surface of the silicon nitride particles to from silicate liquid phase to accelerate the densification
通过xrd 、 sem 、 tem等测试结果表明，由于同时添加了mgo和ceo _ 2作为助烧剂，其致密化过程为液相烧结，由烧结助剂和si _ 3n _ 4表面的sio _ 2反应形成低熔点的硅酸盐相，促进烧结致密化，冷却后，在晶界形成玻璃体。