- Pbo - b _ 2o _ 3 - sio _ 2 glass reacts with bismuth ruthenate and lead ruthenate is produced as transition layer . the transition layer can make the interface gradually change and the properties of resistors are improved at the same time . based on the study above , the way to get series of pastes was developed
铅硼硅玻璃粉体平均粒径对厚膜电阻的性能影响有一极值点,约为1 . 51 m ,在该点处膜层的方阻值最小,电阻温度系数绝对值最小,重烧变化率最接近零值。 - The average partical size of bismuth ruthenate and pbo - b _ 2o _ 3 - sio _ 2 glass was researched . the smaller bismuth ruthenate partical is , sheet resistivity is lower and temperature coefficient of resistance ( tcr ) is more positive and the refiring change ratio is nearer to zero . the limit size of bismuth ruthenate partical is 0 . 56 m
研究了各相粉体平均粒径对膜层性能的影响,结果表明:钌酸铋平均粒径越小,膜层的方阻值越小,电阻温度系数偏正,重烧变化率越接近零值,球磨工艺的极限平均粒径为0 . 56 m 。 - Bismuth ruthenate and silver were selected as conductor phases and the mixture of calcium oxide - alumina - silicon dioxide ( cao - al _ 2o _ 3 - sio _ 2 ) glass and lead oxide - boron oxide - silicon dioxide ( pbo - b _ 2o _ 3 - sio _ 2 ) glass was selected as inorganic binder phases . it was found that , with the increasing of volume fraction of silver and conductor phase , sheet resistivities descend and there are critical thresholds
实验发现,随着功能相百分含量的增加,电阻膜层的方阻值逐渐减小,存在两个临界阈值,电阻温度系数偏向正值;功能相中银百分含量增加,膜层的方阻值逐渐减小,有一个临界阈值,电阻温度系数偏向正值。