microstrain meaning in Chinese
微应变
Examples
- The mean crystallite size and microstrain of u3o8 in different temperature were also discussed in the paper
文中利用fwhm的变化对材料中的微晶尺寸和点阵畸变进行了一定的分析。 - We analyze the microstrain and density changing of the composite powders during pressing . the density evolution of ti / al composite billet became calm when the pressure get to 1000mp . the technique of vacuum degassing can reduce the content of atmosphere
分析了复合粉在冷压制过程中的微观变形过程,不同压力下的密度变化趋势,表明在冷压制压力达到1000mpa后复合粉预制坯密度变化趋于平稳。 - The results show that the ma can accelerate the diffusion in solids . during the ma process , the size of grain in the sample sharply decreases to 65 . 27nm after 30 minute milling and to 4 . 14nm after 20 hour milling , while the microstrain of the grain increases firstly , reaching the maximum 0 . 422 after 10 hour milling and then decreases
通过试验发现，机械合金化可以加速固态扩散，随着球磨的进行，粉末晶粒尺寸急剧下降， 30分钟后达到65 . 27纳米， 20小时后达到4 . 14纳米；微观应变先增大， 10小时达到最大值0 . 422 ，随后减小。 - The evolution on particle morphology , microstructure , grain size and microstrain of the mixture of ti and al elemental powders during mm has been investigated . it was found that the nanocrystalline composite powders with extremely fine ti / al alternative lamellar structure ( lamella spacing about 0 . 1 ~ 0 . 5 m ) could be prepared by mm using proper processing parameters
研究了ti 、 al单质元素混合粉在机械球磨过程中的颗粒形貌特征、组织结构、晶粒尺寸以及微观应变的变化规律,表明在适当的球磨工艺条件下可获得具有极细层片间距( 0 . 1 ~ 0 . 5 m )的纳米晶ti / al机械复合粉。