	1.	Porous bioglass material was prepared by attempting to add pore former 摘要尝试采用添加造孔剂的方法制备了多孔生物玻璃材料。
	2.	As showed by the results , mpf is advantageous for the stable formation or growth of pre - sintered glass beads , and it can partly guarantee the desired " results of sintering 研究结果表明，利用复配造孔剂有利于颗粒的稳定生成和成长，在一定程度上保证烧结过程达到理想状态。
	3.	The results show that factors affecting the pore diameter of porous materials are the sintering temperature and time , the added quantity of pore former and the granularity of glass powder etc 研究结果表明：烧结温度和时间、造孔剂的用量及玻璃粉体的粒度等都将影响多孔材料的孔径。
	4.	Improvement of power output has also been achieved by increasing the porosity of the anode catalyst layer , so that the co2 produced there can be easily released 本研究还以促进co2气体排放为目标，采用添加造孔剂的方法提高了液体进料dmfc阳极催化剂层的孔隙率，显著地改善了电池性能。
	5.	Abstract : in this paper , the porous - metal nickel was prepared by filling pore - forming material and vacuum sintering process . the influence of pore - forming material on the properties of porous - metal nickel was discussed 文摘:采用添加造孔剂、真空烧结工艺制备了多孔金属镍材料，并主要讨论了造孔剂含量对材料性能的影响。
	6.	Air electrode , in which nh _ 4hco _ 3 is as pore former , is mainly studied in this paper . the manufacturing process of air electrode , the composition of waterproof and gas diffusion layer , the composition of catalysis layer , and two kinds of catalyst were studied by numbers 本文针对以碳酸氢铵为造孔剂的空气电极进行研究,分别对电极制作工艺、防水透气层组成、催化层组成以及两类催化剂进行了初步系统的探索和研究。
	7.	Orthogonal tests of waterproof and gas diffusion were taken to option the mass ratio of composition , and meticulous tests of each factor were taken too . scanning electric microscope was used to observe the surface pattern . finally the best composition was found 实验以正交试验的方式确定了防水透气层组成并对单因素进行了考察,并用sem观察表面形貌,最终确定防水透气层组成活性碳、 ptfe 、造孔剂、乙炔黑的质量比为5 . 00 : 2 . 00 : 6 . 00 : 5 . 00 。
	8.	The material was sintered at 1050 for three hours to get the porous artificial bone , that its apparent porosity was54 % , its volume density was 1 . 28 g / cm3 , and its bending strength was 13 . 25mpa . the results showed that the sintering temperature was reduced by adding bioglass 本研究采用含生物玻璃前驱体粉末原料，添加柠檬酸造孔剂，模压成型，在1050烧结保温3小时，获得了显气孔率为54 、体积密度为1 . 28s cm ~ 3 、抗弯强度为13 . 25mpa的多孔hap人工骨材料。
	9.	Beginning with the analysis of the effects , which are brought by the application of only one kind of pore - former and some other operating factors ( such as sintering temperature , warmth retaining time and so on ) , on the properties of the beads , e . g . , porosity , strength , size distribution of the beads and pores size , etc . , these effects are discussed in detail and the relationship between the factors is studied thoroughly . the use of mpf ( multi - pore - former ) is introduced for the first time , which is of the most importance and significance in this paper 研究从造孔剂选用和烧结过程对颗粒的孔隙率、机械强度、孔径分布及粒度分布的影响入手，找出了造孔剂的种类及含量、烧结温度以及保温时间等因素对最终所得产品颗粒的性能影响及它们之间的相互关系，并首次提出将造孔剂复配使用来对填充法加以改进，无需扩孔处理，即能直接制备宏孔径、高强度、小粒度、比表面大的多孔玻璃载体颗粒。
	10.	The optimum conditions for air electrode preparation were shown as follow : 20 % ptfe and 20 % mno2 in active layer , thickness of active layer 0 . 15 - 0 . 25mm and the ratio of active carbon to ethine black 4 : 1 ; 60 % ptfe in the gas diffusion and waterproof layer , employing na2so4 as pore - making agents , thickness 0 . 35 - 0 . 45mm , colding forming and layer sequence catlytic layer / gas diffusion and waterproof layer / current collector layout ; employing 40 meshed nickel screen as current collector and thermal treatment temperature over 200 确定了制备空气电极的优化工艺条件，催化层中ptfe含量约20 ， mno _ 2的最佳含量约为20 ，催化层中活性炭和乙炔黑的比例为4 ： 1 (质量比) ，厚度在0 . 15 - 0 . 25mm之间。防水透气层中ptfe的含量约为60 ，以无水硫酸钠作为造孔剂，厚度一般为0 . 35 - 0 . 45mm 。电极各层采用催化层/防水透气层/集流体的排布方式，冷压成型，热处理对空气电极的性能影响较大，热处理温度不低于200 。