等轴组织 meaning in English
equiaxed structure
Examples
- When ct20 alloy was tensioned at 20k , the main deformation mechanism in equiaxed microstructure was the slip of dislocations , and in bimodal microstructure the slip of dislocations and a small amount of twinning and in lamellar microstructure a large amount of twinning
Ct20合金20k拉伸变形时，等轴组织主要是位错的滑移起主导作用，双态组织除了位错滑移外还有少量的变形孪晶产生，片状组织中则能观察到数量较多的孪晶。 - When the specimens are deformed in a long time at the optimal superplastic deformation condition , the microstructure is coarsened sharply . if the deformation time is shortened properly or the deformation temperature is decreased appropriately or strain rate is increased , homogeneous and fine equiaxed crystal microstructure can be obtained
在最佳超塑性条件下长时间变形时，合金显微组织将发生明显粗化，适当缩短变形时间、或适当降低超塑变形温度及提高应变速率，可得到均匀细小的等轴组织。 - The studying results indicated that : three typical microstructures were abtained when ct20 alloy were annealed under different temperature , that is , equiaxed microstructure ( annealed at t1 , t2 and t3 ) , bimodal microstructure ( annealed at t4 and t5 ) and lamellar microstructure ( annealed at t6 ) . the effect of microstructure on rt tensile properties was weak , while at 20k was notable
研究表明： ct20合金冷轧态管材通过热处理可以获得三种典型的组织类型，即等轴组织( t1 、 t2和t3制度) 、双态组织( t4和t5制度)和片状组织( t6制度) ；显微组织对ct20合金的室温性能影响不大，而对20k下性能的影响则较明显。