磷酸亚铁 meaning in English
ferrous phosphare
ferrous phosphate
Examples
- Recent development of lifepo4 cathode materials for lithium - ion batteries
锂离子蓄电池正极活性材料磷酸亚铁锂 - Based on decreasing the production cost and enhancing the high rate performance of this material , this paper adopted a two - step solid - state reaction to improve lifepo4 ` s behavior mainly using carbon coated or doped and mg2 + doped method
本文从降低材料生产成本的同时提高材料的大电流放电性能出发,采用球磨高温固相法主要针对碳掺杂/包覆和金属离子掺杂对磷酸亚铁锂进行改性。 - Obviously , it is better than the material prepared by solid - state process : the first discharge capacity is 91mah / g , after 20 cycles the specific capacity is around 81 . 71mah / g . besides , we tried to prepare arrays of nanowires using aao
本文还探索了利用溶胶凝胶法在模板中合成氟磷酸亚铁钠纳米线,发现该法制备的材料初次放电容量高达119mah / g ,循环20次后的放电比容量为110mah / g 。 - It is found that we can more easily obtain the good behavior material under the conditions of 600 sintering temperature 、 ar / h2 inertia atmosphere , after testing the influence of the different sintering temperature and inertia atmosphere during the reactions to the performance of lifepo4
通过测试不同合成温度和不同的焙烧气氛条件对磷酸亚铁锂性能的影响,得出结论:采用600合成温度、在ar / h2混合气体保护下更有利于合成性能良好的磷酸亚铁锂。 - Then we prepared na2fepo4f cathode material coated with carbon by solid - state reaction . as cathode material , the first discharge capacity is 111mah / g and the capacity reduces to 102 . 1mah / g after 20 cycles . ultrafine na2fepo4f powders synthesized by a sol - gel process also shows a good electrochemical performance
随后采用在材料表面覆碳的方法对氟磷酸亚铁钠进行改性,结果表明当掺碳量为5 %时,电池的首次放电比容量为111mah / g ,第20次的放电比容量为102 . 1mah / g 。