焊缝厚度 meaning in English
actual weld throat thickness
actual weld-throat thick-ness
seam welding throat thickness
throat depth/ throat thickness
weld thickness
weld-throat thickness depth
Examples
- When the welding current is added , the quality of heat of the arc will increase , so both the volume of molten puddle and the depth of arc crater will all increase , and the weld depth will increase when the weld is cooling
焊接电流增加时，电弧的热量增加，因此熔池体积和弧坑深度都随电流增加，所以冷却下来后，焊缝厚度就增加。 - The welding speed have evident effection on weld depth and weld width , when welding speed is added , both weld depth and weld width will decrease , for the inputed heat per time is limited
焊接速度对焊缝厚度和焊缝宽度有明显的影响，当焊接速度增加时，焊缝厚度和宽度都大为下降，这是因为焊接速度增加时，焊缝中单位时间内输入的热量减少。 - Weld positioning under load without installation , seam thickness of the seam thickness of not less than two - thirds of the design , not to exceed 8 mm , should not be less than 25 mm in length weld , located in welds inside
安装定位焊缝不需承受荷载时,焊缝厚度不少于设计焊缝厚度的2 / 3 ,且不大于8 ? ,焊缝长度不宜小于25 ? ,位置应在焊道内.安装焊缝全数外观检查,主要的焊缝应按设计要求用超声波探伤检查内在质量.上述检查均需做出记录 - Sonic new ideas and views were proposed , such as regulation on general welding procedure qualification and its method of application , welding procedure qualification between heat exchange tube and tube sheet assessmented by the thickness of fillet weld , and so on
本文还首次提出一些新思路、新观点，如母材、焊材分类细则以及标准以外材料分类要有分类报告佐证；通用的焊接工艺评定规定及使用方法；换热管与管板的焊接工艺评定是评定角焊缝厚度；气瓶焊接工艺评定是两个类型评定的结合，也可以分别评定。