无压烧结 meaning in English
loose sintering
pressureless sintering
pressurelesssintering
Examples
- Effect of phase transformation and grain size on pressureless sintering behavior for tio2 ceramics
相变和晶粒尺寸对二氧化钛陶瓷无压烧结行为的影响 - The la1 - xsrxmno3 powder has been sintered by constant pressure sintering , heat pressure sintering ( hp ) and spark plasma sintering ( sps )
通过无压烧结，热压烧结和sps烧结工艺对lal . xsrxmno3粉末进行烧结，其中sps烧结在900 ，保温1omin得到的烧结样品致密化程度最好。 - Mas precursor powders were uniaxially pressed at 100 mpa employing a lubricated steel cylindrical mold . after sintering at 1450 for 2 hours , single - phase cordierite ceramic is prepared , and its relative density is 95 . 1 %
Mas先驱体粉末在100mpa的轴向压力下成型后，经1450无压烧结2小时，得到单相堇青石陶瓷，其致密度达95 . 1 。 - In the section of non - pressing sintered , the influence of different raw material system and sintered temperature on the phase composition of the material were studied . and two conclusions were achieved . the one is that it is good for phase composition design and control because the final phase composition of the material fabricated by ti , sic and c raw material system is comparatively stable
在无压烧结阶段，研究了原料体系与工艺制度对材料物相组成的影响，结果表明使用ti 、 sic 、 c的原料体系得到的材料最终物相组成比较稳定，有利于进行材料组成设计与控制； 1500得到的材料中的杂质相含量较少，是比较合适的反应温度。