固化程度 meaning in English
degree of cure
state of cure
Examples
- It was found that only intercalating nanocomposites be prepared by melt polymerization , and the organoclays deintercalated when curing took place
实验表明熔融聚合只能得到插层型纳米复合材料，并且随着固化程度的提高，粘土将会发生脱剥离现象。 - By use of differential scanning calorimetry ( dsc ) for analysis of the glass transition temperature , the influence of latex particle size , curing temperature and reactivity of curing agents on the curing extent of the waterborne epoxy / amine system have keen studied
摘要以差示扫描量热( dsc )为主要研究手段，通过对涂膜的玻璃化转变温度的分析，研究了乳胶粒粒径、固化温度和固化剂的活性对塑胺水性环氧双组分体系固化程度的影响。 - It is found that the smaller site of latex particle results in higher curing extent of waterborne epoxy / amine system , and the system has a optimized curing temperature , at which it shows the best comprehensive properties of the film and highest curing extent , and the curing extent with second amine higher than that with primary amine
研究发现，水性环城树脂乳胶粒粒径越小，水性环氧体系的固化程度越高；型水性环氧体系的固化存在最佳的固化温度，在此温度下，体系的固化反应程度最高，涂膜的综合性能最佳；仲胺类固化剂与环氧树脂乳胶粒的固化程度比伯胺类固化剂的高。 - As to epoxy / toa / org - mmt system , the reaction order was 0 . 9 and active energy was 66kj / mol by kissinger method ; and a similar result was obtained by ozawa method . the curing reaction was controlled clearly by diffusion mechanism in the later stage of curing reaction without addition of org - mmt , which leads to the increment of active energy with extend of curing ; as to the curing system with addition of org - mmt , the value of active energy was always kept the same level , which can be explained by the catalytic function of amine salt inserted in the galleries of org - mmt
对于环氧桐油酸酐有机蒙脱土固化体系用kissinger方法看到固化体系的反应级数均为0 . 9左右，表观活化能值为66kj mol ； ozawa方法的处理结果与之近似，但从ozawa方法可以看到未加入有机蒙脱土的体系在反应后期固化反应明显受扩散控制，表现为活化能随固化程度的增加而增加；而加入有机蒙脱土的体系，其表观活化能则自始至终表现的较为均匀。 - As the content of vermiculite minerals increased , the content of the " intercalated " shape , in which crystal gallery breadth was about of 40nm , also increased . in the curing reaction processing of polybenzoxazine / vermiculite hybrid nanocomposites intercalated with bisphenol a type precursor . according to the content of vermiculite minerals , while different shape of crystal was forming , these crystals were retarding the heat ring - opening polymerization of bisphenol a type precursors in the nanocomposites
通过对双酚a型ben蛭石纳米插层物固化过程的分析：不同蛭石含量的插层物，在形成不同纳米分散状态固化结构的过程中，蛭石晶片对双酚a型ben的热开环聚合有明显不同的阻碍作用，蛭石含量为3的插层物160的凝胶化时间较纯树脂的延长约7min ，活化能高约8kj mol ，固化反应热晗低约14j g ，使得固化物的固化程度较纯树脂低约10 ，阻碍作用最大，其它含量的次之。