amorphization meaning in English
非晶体化
无定形化
Examples
- The theoretical prediction of amorphization for iron based binary by mechanical alloying
基二元合金机械合金化致非晶化的理论预测 - This in turn causes a more profound modification of the etched surface , e . g . , due to roughening or amorphization
这将导致对于刻蚀表面的严重修正，譬如粗糙度和非晶化。 - However , the peak damage ~ 320dpa occurs at a depth of about 20nm in 1 1017 cm - 2ni + - implanted al2o3 , which leads to amorphization
然而相同注量的ni ~ +注入al _ 2o _ 3在约20nm位置产生损伤最大值320dpa ，样品明显发生非晶化转变。 - Raman spectra of pp during pan - milling indicates that the amorphization of pp was resulted from molecular motion , chain deformation and deterioration of packing regularity caused by deformation under stress
二、将磨盘型力化学反应器应用于金属的碾磨粉碎，碾磨25次后，部分铁粒子的尺寸为40 ? 120nm 。 - The crystalline structure changes of pp induced by pan - milling were characterized by x - ray diffraction and raman spectroscopy . xrd analyses show that when pp was co - milled with uhmwpe , crystal transformation of pp occurred , its crystallinity and crystallite size decreased , whereas , only slight reduction of crystallinity and crystallite size were observed and no crystal transformation was found when pp was co - milled with wtr chips , and amorphization of pp was strongly enhanced by co - milling pp with iron
采用x -射线衍射研究了聚丙烯碾磨粉碎过程微观结构变化， uhmwpe存在下pp发生晶型转变、结晶度降低和晶粒尺寸减小；弹性材料wtr抑制pp塑性变形，碾磨导致分子堆积有序区域膨胀，晶面间距增大，结晶度下降；刚性材料金属铁与pp产生强烈摩擦，加快晶粒细化，晶格破裂导致非晶化。